ASO-Joint-Tapes-2000-S_Product_Information_GB_4815.pdf
2 页数
172.8 KB
Download
<h1>ASO-Joint-Tapes-2000-S_Product_Information_GB_4815.pdf</h1> <p>Product information <br />Waterproof Joint-Tape and pre-formed pieces</p> <p>ASO®-Joint-Tape-2000-S <br />ASO®-Joint-Tape-2000-S-Corners <br />Waterproof Joint-Tape and corner pieces</p> <p>Technical Data: <br />Basis: <br /> </p> <p>composite material <br />fleece-membrane-fleece</p> <p>Colour: </p> <p>white with SCHOMBURG lettering</p> <p>Thickness: <br /> </p> <p>approx. 0.45–0.66 ± 0.1 mm <br />Internal/external angles 0.5 mm ± 0.1 mm</p> <p>Weight: <br /> <br /> </p> <p>approx. 270–340 g/m² <br />Internal angles 10–20 g/piece <br />External angles 10–20 g/piece</p> <p>Tolerated movement <br />accommodation: </p> <p>max. 30% of the joint width</p> <p>Bursting pressure: </p> <p>> 1.5 bar</p> <p>Sd value: </p> <p><2m</p> <p>Temperature resistance: </p> <p>-22 °C to +90 °C</p> <p>UV resistance to <br />DIN EN ISO 4892-2: </p> <p>minimum 500 hrs</p> <p>Reaction to fire: </p> <p>B2</p> <p>Packaging: </p> <p>Joint-Tape: Width 12 cm and 20 cm, <br />± 3 mm <br />Rolls 20 cm at 25 m and 50 m <br />Rolls 12 cm at 50 m</p> <p> <br /> </p> <p>Joint-TapeCorners: 30 pieces per box <br />Internal and external <br />angles14 cm × 14 cm</p> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold (Germany) <br />phone +49-5231-953-00 <br />fax <br />+49-5231-953-108 <br />email export@schomburg.de <br />www.schomburg.com</p> <p>TS/CoS/JD</p> <p>Areas of application: <br />• ASO®-Joint-Tape-2000-S is used for forming waterproof <br />movement joints and junctions in waterproof membranes such <br />as e.g. SANIFLEX, SANIFIN, AQUAFIN®-1K-flex, <br />AQUAFIN®-2K, AQUAFIN®-2K/M, AQUAFIN®-RS300, <br />ASOFLEX-AKB and ADF®-Balkonfolie. <br />• ASO®-Joint-Tape-2000-S fulfills the requirements of the DIBt <br />test principles and the ZDB data sheet “Bonded waterproof <br />membranes”, which are valid for wet duty classes A, B and C <br />and is used particularly in commercial kitchens, therapy <br />pools, swimming pools and heavy duty areas. <br />• ASO®-Joint-Tape-2000-S is easy to use and forms an integral <br />bond with the named waterproof membranes.</p> <p>> 600 %</p> <p>48/15</p> <p>Elongation, transverse <br />to DIN 527-3: </p> <p>Subject to changes. Consult current technical data sheet for most recent information.</p> <p>Breaking force, longitudinal <br />to DIN 527-3: <br />> 116 N / 15 mm <br />Breaking force, transverse <br />to DIN 527-3: <br />> 107 N / 15 mm</p> <p>2 05939</p> <p>ASO®-Joint-Tape-2000-S <br />ASO®-Joint-Tape-2000-S-Corners <br />Special joint tape for highly <br />demanding situations <br />and heavy duty exposure</p> <p>Product application: <br />Using the waterproof membrane, bond ASO®-Joint-Tape-2000-S or <br />ASO®-Joint-Tape-2000-S internal/external angles for use in corners, at the <br />transition between wall and floor as well as interface joints, to the <br />prepared area without voids or folds. Where structural movement joints / <br />movement joints cross over, ASO®-Joint-Tape-2000-T sections or <br />ASO®-Joint-Tape-2000 crosses are available, which permit them to be <br />laid in a looped formation at cross over points. Butt joints must be <br />overlapped by 5 to 10 cm. Ensure that a watertight connection between <br />the wall and the surface applied waterproof membrane is produced. <br />1. Coat both sides of the joint to be bridged with the waterproof <br />membrane to a width of at least 2 cm wider than the waterproof tape, <br />e.g. with a 4 – 6 mm notched trowel. <br />2. Then thoroughly work the joint tape, without voids or folds, into the <br />waterproof membrane using a steel trowel or pressure roller. Ensure <br />that, as far as possible, a full bed and wetting out is achieved. Bonding <br />must be performed in such as way as to exclude the migration of water <br />behind the joint tape. <br />3. The joint tape is to be worked into movement joints as a loop. <br />4. Overlap butt joints within joint tape sections or at interfaces with all joint <br />tape pre-formed pieces and angles by a minimum of 5 to 10 cm and <br />bond with the waterproof membrane, without voids or folds. Overcoat <br />with the chosen waterproof membrane.</p> <p>Properties: <br />• Composite material <br />• Water vapour permeable <br />• Highly resistant to aggressive <br />media <br />• Guarantees the quick drying of <br />adhesives and waterproof <br />membranes, which contain <br />water <br />• Particularly elastic and tear <br />resistant <br />• Thin build-up <br />• UV stabilised</p> <p>Application: <br />All usual substrates, which are suitable to take a waterproof membrane <br />and tiled finish under the relevant exposure class (ZDB data sheet <br />“Bonded waterproof membranes”) and which have been professionally <br />prepared. Fine, non-penetrating cracks on the surface of < 0.1 mm are <br />permitted.</p> <p>1 Load-bearing substrate</p> <p>2 ASO®-Joint-Tape-Technologie</p> <p>3 Priming the substrate, e.g. with <br />ASO®-Unigrund</p> <p>4 Bonding ASO®-Joint-Tape-2000-S-Corners <br />in the first coat of the waterproof membrane</p> <p>5 Bonding ASO®-Joint-Tape-2000-S in the <br />first coat of the waterproof membrane</p> <p>6 Bonding ASO®-Joint-Sleeve-Wall in the first <br />coat of the waterproof membrane</p> <p>7 Bonding ASO®-Joint-Sleeve-Floor in the first <br />coat of the waterproof membrane</p> <p>8 Bonded ASO®-Joint-Tape technology</p> <p>Chemical resistance after 7 days storage at +22° C <br />with the following chemicals: <br />Hydrochloric acid 3 %, Sulphuric acid 35 %, <br />Citric acid 100 g/l, Lactic acid 5 %, <br />Potassium hydroxide 20 %, Sodium hydroxide 0.3 g/l, <br />Salt water 20 g/l (sea salt)</p> <p>9 Overcoating the ASO®-Joint-Tape <br />technology and waterproofing the surface <br />with a suitable SCHOMBURG bonded <br />waterproof coating</p>