THERMOPAL-ULTRA_201491_Englisch.pdf
4 Pages
1.44 MB
Download
<h1>THERMOPAL-ULTRA_201491_Englisch.pdf</h1> <p>Technical data sheet <br />THERMOPAL®-ULTRA <br />WTA rapid-setting restoration plaster</p> <p>Material number</p> <p>Package type</p> <p>Colour</p> <p>Units / pallet</p> <p>Pc/package</p> <p>201491004</p> <p>25 kg, bag</p> <p>Grey</p> <p>42,000</p> <p>1,000</p> <p>Areas of application <br />For restoring living spaces <br />for private and commercial areas <br />in case of a high salt load in the masonry work <br />in the event of moisture damage caused by condensation <br />for building sites under time pressure <br />for base surfaces <br />for interior and exterior use</p> <p>Product features <br />Restoration plaster mortar (R) after DIN EN 998-1 <br />Cementitious pre-blended dry mortar <br />WTA-certified <br />Rapid, reactive binding even with critical site conditions <br />Application up to 30-mm layer thickness in one application step</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />1/4</p> <p>27/03/2026</p> <p>Technical data sheet <br />THERMOPAL®-ULTRA <br />Advantages <br />Extremely low shrinkage <br />Rapid build-up of hydrophobicity <br />Sulphate resistant <br />Soon ready for rubbing down <br />Vapour permeable</p> <p>Technical Data <br />Material properties <br />Product components <br />Base material <br />Consistency <br />Grain size max <br />Bulk density of fresh mortar <br />Compressive strength (classification DIN EN 998-1) <br />Tensile adhesion strength (28 days) <br />Capillary water absorption EN 998-1 <br />Water vapour diffusion coefficient µ <br />Water penetration <br />Thermal conductivity λ (Lambda) <br />Durability (frost resistance) <br />Classification of the reaction to fire in accordance with DIN EN 13501-1</p> <p>1 component system <br />Pre-blended dry mortar <br />Filler consistency <br />< 2 mm <br />approx. 1 kg/dm³ <br />CS II <br />≥ 0.08 N/mm² <br />> 0.3 kg/m² <br />< 15 <br />≤ 5 mm <br />approx. 0.27 W/m * K <br />Resistant when applied in accordance with TM <br />A1</p> <p>Mixing <br />Mixing time <br />Water addition <br />Yield, litre</p> <p>approx. 3 minutes <br />From 7.0 l to 7.5 l per 25 kg <br />approx. 30 l per 25 kg</p> <p>Application <br />Substrate/application temperature <br />Pot life <br />Method of application, max. layer thickness per application step <br />Consumption pro m² and cm layer thickness <br />Hardening process per 24 hours</p> <p>approx. 5 - 30 °C <br />approx. 45 minutes <br />up to 30 mm <br />approx. 9 kg/m² <br />min. 1 mm</p> <p>Processing equipment <br />Aids/tools <br />Stirrer (approx. 500-700 rpm) <br />Suitable mixing paddle <br />Trowel <br />Flat trowel <br />Plasterer’s darby <br />Grid float <br />Spray equipment</p> <p>Manual processing <br />Can be smoothed with a smoothing tool <br />Can be trowelled off</p> <p>Machine application <br />THERMOPAL®-ULTRA can be mechanically applied. For precise information, see the additional Technical Information No. 43.</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />2/4</p> <p>27/03/2026</p> <p>Technical data sheet <br />THERMOPAL®-ULTRA <br />Preparing the substrate <br />Requirement for substrate <br />1. Free of adhesion inhibiting substances <br />2. Pore open <br />3. Load-bearing</p> <p>Preparing the details <br />Scrape out crumbly masonry joints approx. 2 cm deep and clean the surfaces mechanically.</p> <p>Preparing the surface <br />1. Remove old, damaged plasters, paints or coatings from the substrate up to 80 cm above the visible damaged area or the area delimited through <br />inspections. The substrate must be prepared so that it is load-bearing. <br />2. Pre-treat it with ESCO-FLUAT in case of salt contamination. Apply a semi-covering splatterdash coat of THERMOPAL-SP as a bond coat (degree <br />of coverage approx. 50%). In conjunction with mineral waterproofing slurries, apply the adhesive splatterdash coat over the entire surface with <br />100% coverage.</p> <p>Application <br />Measures depending on the degree of salting after WTA</p> <p>Mixing <br />1. Pour the required quantity of water into a clean mixing bucket. <br />2. Completely add the powder and mix until homogeneous and free from lumps. <br />3. The mixing time is ca. 3 minutes. <br />4. After a short activation time, stir again.</p> <p>Application <br />1. THERMOPAL®-ULTRA can be applied on the surface in a single application step with a layer thickness up to 30 mm. <br />2. For thicker layers, render in several layers. <br />3. In this case, strike off the previous layer with a plasterer’s darby, and immediately after stiffening, roughen up horizontally and allow to dry. <br />4. Striking off is done with a suitable tool (float, trowel or plasterer’s darby), depending on the application, within the pot life. <br />5. After sufficient standing time, the surface may be felt boarded matt damp or rubbed down. <br />6. Alternatively, the surface can also be treated with a grid float. Grid floating is performed depending on the ambient conditions. <br />7. If necessary, the plaster surface can be overcoated after one day with THERMOPAL® FS33 fine mortar.</p> <p>Storage conditions <br />Storage <br />Store in a cool and dry place. Min. 9 months in the original canister. Promptly use opened container.</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />3/4</p> <p>27/03/2026</p> <p>Technical data sheet <br />THERMOPAL®-ULTRA <br />Notes <br />Protect surfaces that are not to be treated from the effects of THERMOPAL®-ULTRA! <br />Very damp substrates may require longer waiting times before they can be rubbed off. <br />With low strength substrates, a corrosion-resistant plaster base must be attached mechanically to the substrate prior to plastering. (Cannot be <br />used with internal waterproofing). <br />With difficult site conditions (e.g. inhomogeneous masonry work, waterproofed masonry work, use in exterior area under changing weather <br />conditions and thick-layer plaster build-ups, etc.), an alkali-resistant glass scrim with a mesh size of 7 × 7 mm or 10 × 10 mm can be used to <br />increase the cracking resistance. The inlay of the plastering fabric is applied in the upper third of the plaster layer. <br />Rubbing prematurely or too intensively causes a binder concentration on the surface and can cause stress cracks. <br />Observe the WTA "Restoration plaster systems" data sheet for planning and implementing of restoration measures. <br />Smooth surfaces are achieved by trowelling with THERMOPAL®-FS33. <br />Protect from strong solar radiation and draughts. <br />Highly vapour permeable dispersion silicate paints must be used for the colour design.</p> <p>Observe applicable safety data sheet! <br />Explanations <br />Conformity / Declaration / Verification</p> <p>The rights of the buyer with regard to the quality of our materials are based on our terms and conditions of sale and delivery. Our technical advice team will be happy to advise you <br />in the case of requirements that exceed the scope of the application described here. In order to be binding, a legally binding written confirmation is required. The product description <br />does not release the user from a duty of care. Lay a test area in the event of uncertainty. This version becomes invalid in the event of a new version being issued.</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />4/4</p> <p>27/03/2026</p>