LIGHTFLEX_Product_information_GB_2616.pdf
2 Pages
267 KB
Download
<h1>LIGHTFLEX_Product_information_GB_2616.pdf</h1> <p>Product information <br />Tile adhesives/Thin-bed mortars</p> <p>LIGHTFLEX® <br />Multifunctional flexible adhesive <br />grey, C2 TE S1</p> <p>Application/ <br />substrate temperature: </p> <p>+5°C to +25°C</p> <p>Open time*: </p> <p>approx. 30 mins</p> <p>Foot traffic/ready to <br />grout*: </p> <p>after approx. 24 hrs</p> <p>Consumption: <br /> <br /> </p> <p>approx. 1.3 kg/ m² with a 6 mm notched trowel <br />approx. 1.8 kg/ m² with an 8 mm notched trowel <br />approx. 2.2 kg/ m² with a 10 mm notched trowel</p> <p> <br /> <br /> </p> <p>approx. 1.9 kg/ m² with an 8 mm Flowline trowel <br />approx. 2.7 kg/ m² with a 10 mm Flowline trowel <br />approx. 3.2 kg/ m² with a 12/20 mm medium bed trowel</p> <p>Full service conditions*: </p> <p>after approx. 7 days</p> <p>Reaction to fire: </p> <p>A1/A1fl</p> <p>Packaging: </p> <p>15 kg plastic bag</p> <p>*at +20 °C and 65 % relative humidity</p> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold <br />04 <br />2 01005 <br />EN 12004 <br />LIGHTFLEX® <br />Cement-based adhesive with increased performance for <br />the installation of tiles in interior and exterior areas <br />C2 <br />Reaction to fire: <br />Bond strength, as <br />Tensile adhesion after dry ageing: <br />Durability, as <br />Tensile adhesion strength after <br />water immersion: <br />Tensile adhesion strength after <br />heat ageing: <br />Tensile adhesion strength after <br />freeze/thaw cycles: </p> <p>Class A1/A1fl <br />≥ 1 N/mm²</p> <p>≥ 1 N/mm² <br />≥ 1 N/mm² <br />≥ 1 N/mm²</p> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold (Germany) <br />phone +49-5231-953-00 <br />fax <br />+49-5231-953-108 <br />email export@schomburg.de <br />www.schomburg.com</p> <p>TS/CoS/JD</p> <p>As a thin-bed adhesive: <br />7.5 – 8.1 litres water: 15 kg LIGHTFLEX® <br />As a medium-bed adhesive: <br />7.4 – 7.9 litres water: 15 kg LIGHTFLEX® <br />As a smoothing mortar: <br />7.4 – 7.9 litres water: 15 kg LIGHTFLEX® <br />As a flow-bed adhesive: <br />10.2–10.8 litres water: 15 kg LIGHTFLEX®</p> <p>26/16</p> <p>Areas of application: <br />• LIGHTFLEX® is an extremely high yield, variable use thin-bed, <br />medium-bed or flow-bed flexible adhesive for the installation of <br />large format porcelain (also on walls), vitrified and <br />earthenware tiles and other ceramic finishes, mosaics and <br />natural stone, that is not sensitive to discolouration nor is <br />translucent. <br />• LIGHTFLEX® can also be used for the preparation of substrates <br />as a levelling compound or repair mortar at thicknesses up to <br />15 mm. <br />• LIGHTFLEX® is suited for tiling to all substrates in accordance <br />with DIN 18157, part 1, e.g. concrete, aerated concrete, <br />plaster/render, cement-based and calcium sulphate based <br />heated and unheated (flow) screeds, masonry work, moisture <br />resistant plasterboard and gypsum fibre boards, composite <br />materials in expanded or extruded polystyrene with a mortar <br />coating and reinforcement layer embedded, etc. <br />• F or tiling over mineral-based or dispersion-based <br />SCHOMBURG bonded waterproof membranes.</p> <p>Mixing ratio: <br /> <br /> <br /> <br /> <br /> <br /> <br /> </p> <p>Subject to changes. Consult current technical data sheet for most recent information.</p> <p>Technical Data:</p> <p>2 05023</p> <p>LIGHTFLEX® <br />Multifunctional flexible <br />adhesive <br />grey, C2 TE S1 <br />Properties: <br />• 4 in 1 <br />Thin-bed, medium-bed and flow-bed <br />adhesive as well as repair and <br />levelling mortar up to a thickness of <br />15 mm <br />• Good sag resistance <br />• Up to 90% reduced dust* <br />• Up to 65% greater coverage* <br />• Especially easy to use with greater <br />yield <br />• For large format porcelain tiles <br />incl. walls <br />• For heated screeds <br />• For interior and exterior use <br />• Tested to <br />DIN EN 12004 C2 TE <br />DIN EN 12002 S1</p> <p>ve</p> <p>ry</p> <p>1 Cleaned, load-bearing substrate ready for <br />tiling</p> <p>2 Priming the substrate, e.g. with <br />ASO®-Unigrund</p> <p>3 Adding the adhesive to a clean mixing <br />bucket</p> <p>4 Mixing the adhesive</p> <p>5 Setting out the wall</p> <p>6 Combing out the adhesive bed</p> <p>7 Fixing the wall tiles</p> <p>8 Priming the substrate, e.g. with <br />ASO®-Unigrund</p> <p>9 Setting out the floor</p> <p>10 Combing out the adhesive bed</p> <p>12 Laying the floor tiles</p> <p>13 Finished area ready for use</p> <p>Mixing ratio: highly deformable (relates to class C2 S2, <br />deformation > 5 mm): <br />4.17 kg UNIFLEX®-B : approx. 4.0 litres water : 15 kg LIGHTFLEX®. <br />Application: <br />The substrate must be dry, load bearing sufficiently flat and free from <br />penetrating cracks and separating substances such as oil, paint, laitance and <br />loose components. The substrate surface must have a largely closed texture <br />and its condition must be appropriate for its type. For tiling, the substrate, its <br />preparation and product application must conform to DIN 18157, <br />part 1. Prime absorbent substrates with ASO®-Unigrund. <br />Heated floors are to b e heated prior to installing tiles. The readiness of a <br />substrate to receive finishes is to be determined by the carbide (CM) <br />method and may not fall below the following values: <br />•CT ≤ 2.0% (when installing large format tiles 1.5%) <br />•CA/CFA unheated ≤ 0.5%, heated ≤ 0.3%</p> <p>io n</p> <p>* compared with conventional cement-based <br />adhesives without lightweight aggregates</p> <p>Product preparation: <br />Mix LIGHTFLEX with clean water in a clean mixing bucket until <br />homogenous. Mixing ratio: <br />• as a thin-bed adhesive: 7.5 – 8.1 litres water: 15 kg LIGHTFLEX® <br />• as a smoothing mortar: 7.4 – 7.9 litres water: 15 kg LIGHTFLEX® <br />• as a mesium-bed adhesive: 7.4 – 7.9 litres water: 15 kg LIGHTFLEX® <br />• as a flow-bed adhesive: 10.2 – 10.8 litres water: 15 kg LIGHTFLEX® <br />Allow to stand for 4 minutes, then mix thoroughly through once again. <br />When using as a flow-bed adhesive firstly mix LIGHTFLEX® with approx. 8 <br />litres of water and subsequently mix in the remaining water until a pourable <br />consistency is achieved. Do not mix more material than can be used within <br />the pot life. Spread the mixed adhesive over the substrate and dependent <br />on the tile format comb through with the appropriate notched trowel. Fix <br />the finishing material within the adhesive open time. When installing large <br />format tiles, we recommend that LIGHTFLEX® is modified with UNIFLEX®-B. <br />Modification with this elastifier improves the deformability and tensile <br />adhesion of LIGHTFLEX®. Dependent on the level of modification, S2 <br />deformation class can be achieved which is particularly recommended for <br />larger tiles. This considerably compensates for shear stresses, which can <br />lead to delamination in unfavourable exterior conditions. UNIFLEX®-B is <br />mixed with water for improved application and then mixed with <br />LIGHTFLEX® until homogenous.</p> <p>l o w e m iss</p> <p>11 Applying a contact layer with large <br />format tiles</p>
