THERMOPAL-WSP-120_201493_Englisch.pdf
3 页数
880.5 KB
Download
<h1>THERMOPAL-WSP-120_201493_Englisch.pdf</h1> <p>Technical data sheet <br />THERMOPAL®-WSP-120 <br />Cementitious thermal insulation and restoration plaster</p> <p>Material number</p> <p>Package type</p> <p>Colour</p> <p>Units / pallet</p> <p>Pc/package</p> <p>201493001</p> <p>50 l, bag</p> <p>Grey</p> <p>24</p> <p>1</p> <p>Areas of application <br />For restoring living spaces <br />for private areas <br />For high quality utility areas <br />For energy-efficient restoration <br />For wall and floor surfaces <br />For mould remediation <br />in the event of moisture damage caused by condensation <br />for interior and exterior use</p> <p>Product features <br />Cementitious thermal insulation plaster <br />Thermal insulation <br />Humidity regulating <br />Non-combustible <br />For layer thicknesses up to 120 mm <br />Machine-accessible</p> <p>Advantages <br />Climate-regulating <br />Thermal insulation <br />Vapour permeable</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />1/3</p> <p>09/02/2026</p> <p>Technical data sheet <br />THERMOPAL®-WSP-120 <br />Technical Data <br />Material properties <br />Base material <br />Consistency <br />Grain size max <br />Bulk density of fresh mortar <br />Compressive strength (classification DIN EN 998-1) <br />Water vapour diffusion coefficient µ <br />Thermal conductivity λ (Lambda) <br />Classification of the reaction to fire in accordance with DIN EN 13501-1</p> <p>Pre-blended dry mortar <br />Filler consistency <br />< 2.5 mm <br />approx. 0.68 kg/dm³ <br />CS I <br />< 15 <br />approx. 0.076 W/m * K <br />A1</p> <p>Mixing <br />Mixing time <br />Water addition <br />Yield per sack per cm layer thickness</p> <p>approx. 3 - 5 minutes <br />approx. 3.45 m²</p> <p>Application <br />Substrate/application temperature <br />Pot life <br />Method of application, max. layer thickness per application step <br />Consumption per m² and cm layer thickness <br />Curing rate per cm</p> <p>approx. 5 - 30 °C <br />approx. 60 minutes <br />up to 40 mm <br />approx. 11.9 l/m² <br />approx. 2 days</p> <p>Processing equipment <br />Aids/tools <br />Forced paddle mixer <br />Continuous mixer <br />Suitable mixing basket (e.g. Collomix MK 160 mm) <br />Trowel <br />Flat trowel <br />Plasterer’s darby <br />Grid float</p> <p>Manual processing <br />Can be smoothed with a smoothing tool <br />Can be trowelled off</p> <p>Machine application <br />THERMOPAL®-WSP-120 can be mechanically applied. For precise information, see the additional Technical Information No. 43.</p> <p>Preparing the substrate <br />Requirement for substrate <br />1. Free of adhesion inhibiting substances <br />2. Pore open <br />3. Load-bearing</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />2/3</p> <p>09/02/2026</p> <p>Technical data sheet <br />THERMOPAL®-WSP-120 <br />Preparing the surface <br />1. Remove old, damaged plasters, paints or coatings from the substrate up to 80 cm above the visible damaged area or the area delimited through <br />inspections. The substrate must be prepared so that it is load-bearing. <br />2. Highly absorbent, chalky or sandy substrates should be primed with AQUAFIN primer. <br />3. Pre-treat it with ESCO-FLUAT in case of high salt content. Apply a semi-covering splatterdash coat of THERMOPAL-SP as a bond coat (degree of <br />coverage approx. 50%). <br />4. In conjunction with mineral waterproofing slurries such as AQUAFIN-1K or AQUAFIN-RB400, apply the adhesive splatterdash coat over the <br />whole area with 100% coverage. <br />5. When using barrier plasters such as ASOCRET-M30, comb the surface horizontally with an 8 mm notched trowel.</p> <p>Application <br />Mixing <br />1. Pour the required quantity of water into a clean mixing bucket. <br />2. Completely add the powder and mix until homogeneous and free from lumps. <br />3. The mixing time is ca. 3 - 5 minutes. <br />4. After a short activation time, stir again.</p> <p>Application <br />1. THERMOPAL®-WSP-120 can be applied in a single application step up to 40 mm Layer thickness applied on the surface. <br />2. For thicker layers, render in several layers. <br />3. 4. Striking off is done with a suitable tool (float, trowel or plasterer’s darby), depending on the application, within the pot life. <br />5. After sufficient standing time, remove ridges and unevenness using a trowel back or grid float. Alternatively, the surface can be felted or rubbed <br />down to a matt damp finish. <br />6. THERMOPAL®-WSP-120 should always be overcoated with THERMOPAL-FS33 fine plaster.</p> <p>Fine plaster <br />1. THERMOPAL®-WSP-120 may only be reworked after sufficient air drying. <br />2. Depending on the weather and application thickness, this is achieved after 14-20 days (drying time approx. 2 days per cm of insulating plaster). <br />3. Damp substrates extend the standing time to at least 4 weeks. <br />4. After drying, prime the plaster surface with AQUAFIN® primer. <br />5. -</p> <p>Storage conditions <br />Storage <br />Store in a frost-free, cool and dry place. 12 months in the original canister. Promptly use opened container.</p> <p>Notes <br />Protect surfaces that are not to be treated from the effects of THERMOPAL®-WSP-120! <br />Very damp substrates may require longer waiting times before they can be rubbed off. <br />With low strength substrates, a corrosion-resistant plaster base must be attached mechanically to the substrate prior to plastering. (Cannot be <br />used with internal waterproofing). <br />Under difficult site conditions (e.g. inhomogeneous masonry work, waterproofed masonry work, use in exterior area under changing weather <br />conditions and thick-layer plaster build-ups, etc.), an alkali-resistant glass scrim such as ASO®-RSG can be used to increase the cracking <br />resistance. The inlay of the plastering fabric is applied in the upper third of the plaster layer. <br />Rubbing prematurely or too intensively causes a binder concentration on the surface and can cause stress cracks. <br />Protect from strong solar radiation and draughts. <br />Highly vapour permeable dispersion silicate paints must be used for the colour design.</p> <p>Observe applicable safety data sheet!</p> <p>The rights of the buyer with regard to the quality of our materials are based on our terms and conditions of sale and delivery. Our technical advice team will be happy to advise you <br />in the case of requirements that exceed the scope of the application described here. In order to be binding, a legally binding written confirmation is required. The product description <br />does not release the user from a duty of care. Lay a test area in the event of uncertainty. This version becomes invalid in the event of a new version being issued.</p> <p>SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com <br />3/3</p> <p>09/02/2026</p>
