Product information Waterproof Joint-Tape and pre-formed pieces
ASO®-Joint-Tape-2000 ASO®-Joint-Tape-2000-Corners ASO®-Joint-Tape-2000-T-Piece ASO®-Joint-Tape-2000-Crossing Waterproof Joint-Tape and corner pieces for standard applications
Technical Data: Basis:
composite material fleece-membrane-fleece
Colour:
white with SCHOMBURG lettering
Thickness:
approx. 0.37 mm ± 0.1 mm Internal/external angles 0.5 mm ± 0.1 mm
Weight:
approx. 150–190 g/m² Internal angles approx. 3.5 g/piece External angles approx. 5 g/piece
Tolerated movement accommodation:
max. 30% of the joint width
Bursting pressure:
> 2 bar
Sd value:
30 m ± 5 m
Temperature resistance:
-22 °C to +90 °C
UV resistance to DIN EN ISO 4892-2:
minimum 500 hrs
Reaction to fire:
B2
> 60 % > 60 % Joint-Tape: Width 12 cm and 20 cm, ± 2 mm Rolls of 10 and 50 m Joint-TapeCorners: 20 pieces per box Internal and external angles12 cm × 12 cm
SCHOMBURG GmbH & Co. KG Aquafinstrasse 2–8 D-32760 Detmold (Germany) phone +49-5231-953-00 fax +49-5231-953-108 email export@schomburg.de www.schomburg.com
Subject to changes. Consult current technical data sheet for most recent information.
Areas of application: • ASO®-Joint-Tape-2000 is used for forming waterproof movement joints and junctions in waterproof membranes such as e.g. SANIFLEX, SANIFIN, AQUAFIN®-1K-flex, AQUAFIN®-2K, AQUAFIN®-2K/M, AQUAFIN®-RS300 and ASOFLEX-AKB. • ASO®-Joint-Tape-2000 fulfills the requirements of the DIBt test principles and the ZDB data sheet “Bonded waterproof membranes”, which are valid for wet duty classes A, B and C. • ASO®-Joint-Tape-2000 is easy to use, vapour permeable and forms an integral bond with the named waterproof membranes.
> 32 N / 15 mm
TS/CoS/JD
Packaging:
> 50 N / 15 mm
48/15
Breaking force, longitudinal to DIN 527-3: Breaking force, transverse to DIN 527-3: Elongation, longitudinal to DIN 527-3: Elongation, transverse to DIN 527-3:
2 05936 2 05940 2 05941 2 05943 2 05944
v er
y lo
io n
Properties: • Composite material • Water vapour permeable • Highly resistant to aggressive media • Elastic • Tear resistant • Thin build-up • UV stabilised • Very low emissions • Guarantees the quick drying of adhesives and waterproof membranes, which contain water • Fulfills the AgBB scheme requirements.
w e m is
s
Information about the emission level of volatile compounds in indoor air, which pose a health risk by inhalation, on a scale from class A+ (very low emissions) to C (high emissions).
Product application: Using the waterproof membrane, bond ASO®-Joint-Tape-2000 or ASO®-Joint-Tape-2000 internal/external angles for use in corners, at the transition between wall and floor as well as interface joints, to the prepared area without voids or folds. Where structural movement joints / movement joints cross over, ASO®-Joint-Tape-2000-T sections or ASO®-Joint-Tape-2000 crosses are available, which permit them to be laid in a looped formation at cross over points. Butt joints must be overlapped by 5 to 10 cm. Ensure that a watertight connection between the wall and the surface applied waterproof membrane is produced. 1. Coat both sides of the joint to be bridged with the waterproof membrane to a width of at least 2 cm wider than the waterproof tape, e.g. with a 4 – 6 mm notched trowel. 2. Then thoroughly work the joint tape, without voids or folds, into the waterproof membrane using a steel trowel or pressure roller. Ensure that, as far as possible, a full bed and wetting out is achieved. Bonding must be performed in such as way as to exclude the migration of water behind the joint tape. 3. The joint tape is to be worked into movement joints as a loop. 4. Overlap butt joints within joint tape sections or at interfaces with all joint tape pre-formed pieces and angles by a minimum of 5 to 10 cm and bond with the waterproof membrane, without voids or folds. Overcoat with the chosen waterproof membrane.
Application: All usual substrates, which are suitable to take a waterproof membrane and tiled finish under the relevant exposure class (ZDB data sheet “Bonded waterproof membranes”) and which have been professionally prepared. Fine, non-penetrating cracks on the surface of < 0.1 mm are permitted.
1 Load-bearing substrate
2 ASO®-Joint-Tape-Technologie
3 Priming the substrate, e.g. with ASO®-Unigrund
4 Bonding ASO®-Joint-Tape-2000-Corners in the first coat of the waterproof membrane
5 Bonding ASO®-Joint-Tape-2000 in the first coat of the waterproof membrane
6 Bonding ASO®-Joint-Sleeve-Wall in the first coat of the waterproof membrane
7 Bonding ASO®-Joint-Sleeve-Floor in the first coat of the waterproof membrane
8 Bonded ASO®-Joint-Tape technology
Chemical resistance after 7 days storage at +22° C with the following chemicals: Hydrochloric acid 3 %, Sulphuric acid 35 %, Citric acid 100 g/l, Lactic acid 5 %, Potassium hydroxide 20 %, Sodium hydroxide 0.3 g/l, Salt water 20 g/l (sea salt)
9 Overcoating the ASO®-Joint-Tape technology and waterproofing the surface with a suitable SCHOMBURG bonded waterproof coating