Technical Datasheet AQUAFIN®-RS300 Rapid hybrid waterproofing
Material number
Contents
Unit of quantity
Packaging
Colour
204208001
20
KG
Combination packs
light grey
204208003
10
204208010
36
Set
Product features 2 component, cementitious waterproofing slurry Reactive setting Highly flexible and crack bridging Rainproof, can be walked on and overcoated after just ca. 3 hours
Advantages Tested system product Reliable flexibility and drying - even if weather conditions are unfavourable Convenient compaction properties
Areas of use/bonded waterproofing As bonded waterproofing under tiles and boards As bonded waterproofing for water impact class W0-I to W3-I in accordance with DIN 18534 As bonded waterproofing for balconies, loggias, arcades in accordance with DIN 18531 and terraces As bonded waterproofing underwater and for swimming pool building In conjunction with the SCHOMBURG joint tape systems
SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com 1/7
29/06/2023
Technical Datasheet AQUAFIN®-RS300 Existing test certificates Reaction to fire classification report General building approval test certificate for producing liquid bonded waterproofing with tiles and boards in accordance with VVTB seq. no. C 3.27 French cert. VOC EMICODE licence Impermeability to water after storage in concrete-damaging water in accordance with DIN EN 4030-1 Test report in accordance with DIN EN 12004 General building approval test certificate in accordance with Hessian VVTB, June 2018, seq. no. C.3.26 General building approval test certificate for use as waterproofing in transitions on building components made of concrete with high water penetration resistance in accordance with building rules list A, part 2, seq. no. 2.48 Impermeability to water against water pressure that acts on the rear of the coating Crack bridging test at low temperatures (-5 °C) Impermeability to water in accordance with DIN EN 14891
Technical Data Material properties Product components Base material Density (spec. weight) Grain size max Crack classes DIN 18533 Crack bridging ability DIN EN 14891 (at normal and low temperatures) Tensile adhesion strength DIN EN 1542 Crack bridging DIN EN 1062-7 Sd value DIN EN ISO 7783 (H2O) per mm dry layer thickness Vapour diffusion behaviour Water vapour diffusion resistance µ (DIN EN ISO 7783) Watertightness when installed in accordance with PG MDS/AIV Permissible tank depth in accordance with DIN 18535 Classification of the reaction to fire in accordance with DIN EN 13501-1
2 component system Pre-blended dry mortar Polymer dispersion approx. 1.3 kg/dm³ < 1 mm R1-I > 0.75 mm ≥ 1 N/mm² Passed approx. 1.1 m Vapour diffusion behaviour approx. 1100 to 1,5 bar 6m E
Mixing Mix ratio, component A Mix ratio, component B Mixing time Maturing time
1 weight proportion 1 weight proportion approx. 2 - 4 minutes approx. 5 minutes
Application Substrate temperature Pot life Method of application, max. layer thickness per application step Consumption pro m² and mm layer thickness Second application step after waiting time Foot traffic after Ready for covering with tiles Application temperature Overcoat after Pressurised water resilient after Hardening time / light resilience
from 5 °C to 30 °C approx. 45 minutes to 1.5 mm approx. 1.5 kg/m² approx. 3 hours approx. 3 hours approx. 3 hours from 5 °C to 30 °C approx. 3 hours ≥ 3 days approx. 3 days
SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com 2/7
Technical Datasheet AQUAFIN®-RS300 System components according to AbP AIV Primer
Joint Sealing tape
Tile adhesive
ASO-Unigrund-GE ASO-Unigrund-K, blue ASO-Unigrund-S ASO-Dichtband-2000 ASO-Dichtband-2000-Ecken (Innen und Aussen) ASO-Dichtband-2000-S ASO-Dichtband-2000-S-Ecken ASO-Dichtband-2000-Kreuzung ASO-Dichtband-2000-T-Stück ASO-Dichtmanschette-Boden ASO-Dichtmanschette-Wand ASO-Dichtband-120 ASO-Dichtecke-A ASO-Dichtecke-I ASO-Dichtmanschette-W ASO-Dichtmanschette-B AK7P CRISTALLIT-FLEX LIGHTFLEX MONOFLEX MONOFLEX-fast MONOFLEX-FB MONOFLEX-white MONOFLEX-white 3:1 with UNIFLEX-F MONOFLEX-XL SOLOFLEX UNIFIX-S3 UNIFIX-S3-fast ASODUR-EKF
Material consumption Material consumption rate according to the area of application
SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com 3/7
Technical Datasheet AQUAFIN®-RS300 Application technology Aids/tools Flat trowel Broad paint brush Spray equipment Serrated or layer-thickness trowel Stirrer (approx. 500-700 rpm) Trowel
Suitable substrate Concrete, cement screed (CT), floor levelling compounds, calcium sulphate screeds (CA, CAF), mastic asphalt screeds (AS), magnesia screeds (MA) Cement-based plaster, gypsum plaster, cement-lime plaster, lightweight plaster Tile bearing elements, gypsum fibre boards, gypsum boards, raised floors, cement and fibre cement boards, decoupling mats & panels, dry screeds Bonded waterproofing; the suitability of the substrate must be checked and observed, taking into account the planned water impact class of DIN 18534 and DIN 18531. Firmly adhering tiled finishes Old, firmly adhering bituminous substrates
Substrate preparation Requirement for substrate 1. 2. 3. 4. 5. 6.
Even Free of adhesion inhibiting substances Sealed in the surface Pore open Load-bearing Extensively fully grouted
Preparing the details 1. Clean and degrease flanges. 2. Edges are to be chamfered and corners are to be rounded. 3. Depressions > 5 mm and mortar pockets, plaster grooves in brickwork, open butt or bed joints, damaged areas, large pored substrates or uneven masonry work must be levelled in advance with ASOCRET-M30 (cement-based mortar).
Preparing the surface 1. 2. 3. 4.
Extremely absorbent and slightly sandy substrates must be primed with ASO-Unigrund-GE or ASO-Unigrund-K. The primer must be completely dry / must have reacted fully before the subsequent work steps are carried out. Moisture penetration from the rear and intermittent moisture loading from the negative side must be avoided. For waterproofing with moisture penetration from the rear, we recommend pre-sealing with AQUAFIN-1K or ASODUR-SG2/-thix.
Base slab-wall transition 1. While still wet, install a sealing cove with an edge height of at least 4 cm made of ASOCRET-M30. 2. Pre-screen with AQUAFIN®-1K or ASOCRET-M30 in a consistency that is able to screen. 3. After drying, carry out the waterproofing with AQUAFIN®-RS300.
Pipe penetrations 1. In water wear class W 2.1-E, suitable loose fixed flange constructions or tested house entry systems must be used. 2. For the watertight formation of pipe penetrations, the system components of the ASO-Joint-Sleeves are to be used in accordance with their technical data sheets.
SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com 4/7
Technical Datasheet AQUAFIN®-RS300 Usage Mixing 1. Fill approx. 50-60% of the liquid component into a clean mixing bucket and mix with the powder component to produce a homogeneous, lumpfree mass. 2. Finally, add the rest of the liquid component and mix sufficiently. 3. The mixing time is ca. 2 - 4 minutes. 4. After a settling period of ca. 5 minutes, thoroughly homogenise the compound again.
Waterproofing 1. Apply AQUAFIN®-RS300 in a minimum of two application steps ensuring it is free of pores. 2. The material rate is dependent on the required dry film thickness corresponding to the water impact class (see Material rate table). 3. The second application step (and those following) may be completed once the first application step cannot be damaged (see "Technical data > Processing > Second application step after waiting time") 4. An application thickness of more than 2 kg/m² in one application step can lead to cracking. 5. An even layer thickness is achieved using a coating thickness trowel or notched trowel and then smoothing.
Waterproofing bonded with tiles and boards 1. 2. 3. 4.
Floor drains and intersections in the tank area must be provided with suitable flange elements. Tiles or boards are layed with one of the tile adhesives listed in the system components section. The waterproofing layer must be totally hardened at the time of the laying work. Apply the sealing sleeve in accordance with the Technical Data Sheet.
Movement and connecting joints For watertight formation of moving and connecting joints, use ASO-Joint-Sealing Tape system components in accordance with their technical data sheets.
Transitions of watertight concrete building components with an immersion depth of up to 3 m (max. opening width 1.0 mm) 1. Finally, overcoat the bonded joint sealing tapes with the waterproofing at least 15 cm on both sides of the joint. Minimum dry film thickness: 2.5 mm. 2. Alternatively, the transitions can also be sealed using the ASO-Joint-Tape system. 3. Install the selected joint sealing tape in accordance with the technical data sheet. 4. Apply the waterproofing to the prepared substrate to a minimum of 15 cm on both sides of the joint. 5. Guide the waterproofing down approx. 15 cm onto the front surface of the watertight floor slab in the wall/floor transition. 6. Processing takes place in 2 application steps. Total dry film thickness: 4 mm. 7. An even layer thickness is achieved using a 6 to 8 mm notched trowel and then smoothing.
Cleaning tools Rinse tools immediately with water. Dissolve dried material with ASO-R001 and wash off.
Drainage and protection boards for building components in direct ground The waterproofing must be protected against weathering influences and mechanical damage using suitable protective measures in accordance with DIN 18533. 1. The waterproofing must be totally dry. 2. Suitable protection and drainage boards can be fixed in place with COMBIDIC1K in heaps. 3. Perimeter insulation must cover the whole area and be butt jointed with COMBIDIC-2K-CLASSIC or COMBIDIC-2K-PREMIUM. 4. Drainage is carried out in accordance with the specifications of DIN 4095.
Storage conditions Storage Store in a frost-free, cool and dry place. At min. 5 - 40 °C for 9 months in the original canister. Promptly use opened canister.
Disposal Product leftovers can be disposed of in accordance with disposal code AVV 17 01 07 and AVV 08 04 10.
Emission behaviour / building certification systems Very low emissions in accordance with GEV-EMICODE, which normally results in positive evaluations within the scope of building certification systems in accordance with DGNB, LEED, BREEAM, HQE. Maximum quality level 4, lines 7 and 8 in accordance with DGNB criteria "ENV 1.2 Risks to the local environment".
SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com 5/7
Technical Datasheet AQUAFIN®-RS300 Notes AQUAFIN®-RS300 may be plastered and coated with vapour permeable, solvent-free dispersion façade paints or dispersion silicate paints (not pure silicate paints). Silicon resin paints and acrylate-based paints may also be used. On PVC, gunmetal, and stainless steel flanges, ASO® joint sleeves or alternatively ADF® pipe gaskets must be installed without voids or wrinkles and integrated seamlessly into the waterproofing. In case of strong sunlight, work against the movement of the sun in shaded areas. Direct contact with metals such as copper, zinc, and aluminium must be avoided by means of a pore sealed primer. A pore sealed primer is produced via 2 application steps using ASODUR®-GBM (see technical data sheet). In rooms with high humidity and/or insufficient ventilation (e.g. water containers), dropping below the dew point (condensation formation) may occur on the surface. This must be avoided by taking suitable measures such as by using condensation dryers. Direct heating or uncontrolled blowing warm air is not permissible. Protect surfaces that are not to be treated from the effects of AQUAFIN®-RS300! The waterproofing must not be affected by water while it is binding. The effect of water from behind can lead to spalling in case of frost. AQUAFIN®-RS300 can be used to renovate old, firmly adhering substrates containing bitumen, for applications in accordance with WTA datasheet 4-6. The waterproofing must be covered with a scratch coat and, after drying out completely, double-coated with a layer thickness suitable for the load case. In accordance with WTA data sheet 4-6, the foot area and the transition to the splash water building skirt must be stripped back to the mineral substrate beforehand.
Planning, inspection of substrates and building site circumstances, laying, grouting and subsequent care of the work must be done in accordance with the relevant DIN standards and recognised rules of technology (e.g. the ZDB sheets of the Zentralverband Deutsches Baugewerbe e.V.) in the latest version. GISCODE: ZP1 (Komponente A), BSW20 (Komponente B) Annotations Conformity / Declaration / Verification
SCHOMBURG GmbH & Co. KG · Aquafinstr. 2–8 · D-32760 Detmold (Germany) · Tel. +49-5231-953-00 · Fax +49-5231- 953-333 · schomburg.com 6/7
Technical Datasheet AQUAFIN®-RS300 System components (conforming to standards)
The rights of the buyer with regard to the quality of our materials are based on our terms and conditions of sale and delivery. Our technical advice team will be happy to advise you in the case of requirements that exceed the scope of the application described here. In order to be binding, a legally binding written confirmation is required. The product description does not release the user from a duty of care. Lay a test area in the event of uncertainty. This version becomes invalid in the event of a new version being issued.